Turned cast billets of high-temperature nickel base alloys of vacuum melting: diameter 65-90 mm, length up to 850 mm, mass up to 40 kg. Extruded grinded rods of high-temperature nickel base alloys: diameter 20-50 mm, length 200-400 mm, mass 2-5 kg. Long-term temperature strength - min. 50 hours (test temperature 900 0C, constant stress 31-32 kgf/mm2. Room temperature mechanical properties, min.: ultimate strength - 85 kgf/mm2, elongation - 20%, reduction of area - 25%, impact strength - 6 kgf/cm2. 750 0C mechanical properties, min.: ultimate strength - 65 kgf/mm2, elongation - 11%, reduction of area - 15%.

Long-term strength			Room temperature mechanical properties,
Test temperature, 0C	Constant stress, kgf/mm2	Time to failure (min), hours	s в kgf/mm2	s 0,2 kgf/mm2	d (%)	y (%)	a k kgf/mm2
800-1050	11-35	40	85	70	3	4	1